Cite: Tabakov V.P., Shtubov N.S. The influence of the thickness and composition of the top layer of a two-layer coating on the cyclic crack resistance and performance of carbide cutting tools. Bulletin of Ulyanovsk State Technical University. 4(104), 22-26 (2023).

Abstract. The results of studies on the effect of the thickness and composition of the upper layer of two-layer coatings on the cyclic crack resistance and operability of a carbide cutting tool are presented. It is shown that the dependence of cyclic crack resistance and the durability period of a carbide cutting tool on the thickness of the upper layer is extreme, and their maximum values are observed at the same thickness of the upper layer. Varying the thickness of the top layer within 2-6 microns leads to a change in the durability period from 10% to 30%.

Keywords: coating, cyclic crack resistance, cutting tool, durability period.

Цитата: Табаков, В.П. Влияние толщины и состава верхнего слоя двухслойного покрытия на циклическую трещиностойкость и работоспособность твёрдосплавного режущего инструмента / В.П. Табаков, Н.С. Штубов // / Вестник Ульяновского государственного технического университета. – 2023. – № 4(104). – С. 22-26.

Аннотация. Представлены результаты исследований по влиянию толщины и состава верхнего слоя двухслойных покрытий на циклическую трещиностойкость и работоспособность твёрдосплавного режущего инструмента. Показано, что зависимость циклической трещиностойкости и периода стойкости твёрдосплавного режущего инструмента от толщины верхнего слоя имеет экстремальный характер, а их максимальные значения наблюдаются при одной и той же толщине верхнего слоя. Варьирование толщиной верхнего слоя в пределах 2‒6 мкм приводит к изменению периода стойкости от 10% до 30%.

Ключевые слова: покрытие, циклическая трещиностойкость, режущий инструмент, период стойкости.